Markforged H13 Tool Steel v2 – 400CC
Markforged H13 Tool Steel is an excellent choice for high temperature applications that also experience drastic cooling. This, coupled with abrasion resistance and good machinability properties, makes it ideal for high-temperature tooling and wear-resistant pieces. H13 Tool Steel v2 is Markforged’s updated formulation that utilizes a new binder material for superior usability.
$460.00
Product Details
Properties
- Ultimate Tensile Strength (MPa)
- Test (ASTM): ASTM E8
- Result: 1540/1680/1580
- 0.2% Compressive Yield Strength (MPa)
- Test (ASTM): ASTM E8
- Result: 860/1250/1360
- Elongation at Break (%)
- Test (ASTM): ASTM E8
- Result: 4/4.7/14
- Hardness (HRC)
- Test (ASTM): ASTM E18
- Result: 40/45/46
- Relative Density (%)
- Test (ASTM): —
- Result: 94.5/94.5/100
Compatibility
- Metal X