Markforged HSHT Fiberglass CFF – 150CC
Markforged HSHT Fiberglass is defined by two characteristics: high strength (nearly equal to 6061-T6 Aluminum) and strength in high temperatures. Though not as stiff as Continuous Carbon Fiber, Onyx parts reinforced with Markforged HSHT Fiberglass are strong at both low and high temperatures. As a result, HSHT reinforcement is best used for parts in high-temperature environments like molds, autoclaves, and others.
$300.00
Product Details
Properties
- Tensile Strength (MPa)
- Test (ASTM): D3039
- Result: 600
- Tensile Modulus (GPa)
- Test (ASTM): D3039
- Result: 21
- Tensile Strain at Break (%)
- Test (ASTM): D3039
- Result: 3.9
- Flexural Strength (MPa)
- Test (ASTM): D790
- Result: 420
- Flexural Modulus (GPa)
- Test (ASTM): D790
- Result: 21
- Flexural Strain at Break (%)
- Test (ASTM): D790
- Result: 2.2
- Compressive Strength (MPa)
- Test (ASTM): D6641
- Result: 192
- Compressive Modulus (MPa)
- Test (ASTM): D6641
- Result: 21
- Compressive Strain at Break (%)
- Test (ASTM): D6641
- Result: —
- Heat Deflection Temperature (oC)
- Test (ASTM): D648 B
- Result: 150
- Izod Impact – notched (J/m)
- Test (ASTM): D256-10 A
- Result: 3100
- Density (g/cm3)
- Test (ASTM): —
- Result: 1.5