Product SKU: F-MF-1003
Markforged H13 Tool Steel – 200CC
Harder than 17-4 PH Stainless Steel and capable of maintaining material properties at high temperatures, Markforged H13 tool steel is an extremely versatile material to work with. Markforged H13 tool steel can be heat treated to 45 HRC with a UTS of 1500 MPa, and is used by Markforged customers for tool bodies, brazing fixtures, and other parts where hardness or heat resistance are required.
$230.00
Product Details
Properties
- Ultimate Tensile Strength (MPa)
- Test (ASTM): ASTM E8
- Result: 1420/1500/1580
- 0.2% Compressive Yield Strength (MPa)
- Test (ASTM): ASTM E8
- Result: 800/1250/1360
- Elongation at Break (%)
- Test (ASTM): ASTM E8
- Result: 5/5/14
- Hardness (HRC)
- Test (ASTM): ASTM E18
- Result: 40/45/46
- Relative Density (%)
- Test (ASTM): —
- Result: 94.5/94.5/100
Compatibility
- Metal X